fig15

Figure 15. (A) Solvus temperature (T_γ’-solvus) and (B) area fraction (A_{γ’-area fraction}) of γ’ phase in the Co-V-Ta alloy annealed at 800 °C for 600 h, as predicted using machine learning, with the γ and γ’ phase boundaries demarcated in the isothermal section of the Co-V-Ta system at 800 °C established using the CALPHAD approach. (C) Dark-field image and (D) selected area diffraction pattern obtained from the γ+γ’ region in the Co-V-Ta alloy annealed at 800 °C for 648 h. Figure reproduced from Ref.^[83] with permission from Elsevier.